Avèk avanse preparasyon seramik ak teknoloji pwosesis, yon superbly kalifye ekip R & D comprenant pwofesè ceramicstimes ak PhDs te devlope ceramicstimes seramik aspirasyon ajutaj pou ekipman fotovoltaik. Yo te metrize pwosesis kle ki pi enpòtan nan mond lan nan fabrike materyèl seramik avanse, ki gen ladan bòdi, machining billet, sinterizasyon, machining presizyon, ak presizyon fanm k'ap pile, nan adisyon a fòmilasyon poud ak tretman. Ekspè yo mennen ankèt sou materyèl seramik sofistike tankou carbure, nitrid, ak oksid, osi byen ke seramik konpoze; Yo te aplike pou plis pase 30 rive Chinwa. Atik yo lajman vann nan plis pase 50 nasyon ak rejyon atravè lemond epi yo ka Customized ki baze sou desen.

Kondisyon pèfòmans debaz pou bouch seramik

High adsorption stability: Uniform vacuum adsorption force, no offset or slipping of silicon wafers (adsorption force>5kpa).
2. Abrasion resistance: surface hardness>Hv1200, service life>500,000 fwa.
No pollution: material purity >99.5% Al0:, pou fè pou evite Na, K ak lòt enpurte kontaminasyon nan gato Silisyòm.
Segondè rezistans tanperati: pa gen okenn deformation anba anviwònman tanperati ki wo (tankou difizyon gwo founo dife bouch bezwen yo dwe rezistan a plis pase 800'C).
Insulation: volume resistivity>102Q - cm, pou anpeche domaj Electrostatic nan selil la.

Non pwodwi	Bouch seramik pou ekipman fotovoltaik
Materyo	zirkonyòm oksid seramik
Koulè ak gwosè	Customize
Anbalaj	Carton / palèt (dapre kondisyon kliyan)
Tan livrezon	7-30 jou
Atik konsepsyon	Dapre desen oswa echantiyon kliyan an
Karakteristik	Bon kalite, pri ki ba, faktori miltip, delivre ou ki baze sou yon sèl ki pi pre kote ou ye

Seramik pèfòmans paramèt

Nonb	Pèfòmans	Inite
			95alumina	97alumina	99alumina	995alumina	997alumina	998alumina	Zirconia sere alumina	Alumina sere zirkonya
									ZTA	ATZ
1	anfle		95%	97%	99%	995%	997%	998%
2	Densite	g/cm3	3.7	3.8-3.85	3.85	3.9	3.92	3.98	4.0-4.3	Pi gran pase oswa egal a 5.25
3	Fòs fleksib	MPA	304	320	340	370	400	550-600	700	Pi gran pase oswa egal a 650
4	Severite kase	MPA · M1/2	4	4.5	5.6-6	5.6-6	5.6-6	5.6-6	7	Pi gran pase oswa egal a 7
5	Konstan dielèktrik	εr (20 degre, 1MHz)	9.0	9.2	9.5	9.7	9.8	9.9	9.2	9.2
6	Rez nan	GPA	12.8-15	15	15-16	15-16	16.3	16.3-18	13	14.5
7	Rez nan	Mwatye	73-79	79	79-80	79-80	81	81-83	76	78
8	Volim rezistivite	Ω · cm (20 degre)	10 ¹³	10 ¹⁴	10 ¹⁴	10 ¹⁴	10 ¹⁴	10 ¹⁴	10 ¹⁴	10 ¹⁴
9	Modil elastik	GPA	320	330	380	380	380	400	300	280
10	Koyefisyan ekspansyon tèmik	×10-6/k	7.6	7.6	7.6	7.6	5.4-8.4	6.4-8.9	8.3	8.5
11	Fòs konpresiv	MPA	1910	2100	2210	2300	2300	2300	2400	2450
12	Abrasion	g/cm2	0.2	0.1	0.1	0.1	0.1	0.1	0.1	0.1
12	Tèmik konduktivite	W/m × k (20 degre)	20	24-27	34	35	35	38.9	27
13	Rapò Poisson an	/	0.22	0.22	0.22	0.22	0.22	0.22	0.26	0.2
14	Fòs izolasyon	kv/mm	27	28	28	28	30	30	30	30
15	Tanperati	degre	1520-1600	1650	1520	1650	1700	1700	1650	2000